Comportamiento termomecánico de tubos de PEEK para uso en la industria nuclear. (Record no. 27006)

MARC details
000 -LEADER
campo de control de longitud fija 03648mm aa2200325a 44500
000 - LEADER
campo de control de longitud fija aIS/T--161/15
003 - IDENTIFICADOR DE NÚMERO DE CONTROL
campo de control AR-SmCIES
008 - DATOS DE LONGITUD FIJA--INFORMACIÓN GENERAL
campo de control de longitud fija 160323s2015 ag fq d # spa#d
040 ## - FUENTE DE CATALOGACIÓN
Centro catalogador/agencia de origen AR-SmCIES
100 1# - ENTRADA PRINCIPAL--NOMBRE DE PERSONA
Nombre de persona Alcar, Ramiro de la Cruz
245 10 - MENCIÓN DEL TÍTULO
Título Comportamiento termomecánico de tubos de PEEK para uso en la industria nuclear.
246 11 - FORMA VARIANTE DEL TITULO
Título propio/Titulo breve Thermomechanical behavior of PEEK tubes for use in the nuclear industry.
260 ## - PUBLICACIÓN, DISTRIBUCIÓN, ETC.
Fecha de publicación, distribución, etc. 2015.
300 ## - DESCRIPCIÓN FÍSICA
Dimensiones 74 p.
500 ## - NOTA GENERAL
Nota general Cantidad de ejemplares: 1 CD
502 ## - NOTA DE TESIS
Nota de tesis Tesis para optar al título de Magister en Ciencia y Tecnología de Materiales. Director/es: Hermida, Elida Beatríz; Arenas, Claudio Daniel
520 ## - RESUMEN, ETC.
Sumario, etc. El PEEK es un material termoplástico lineal desarrollado para usos específicos en ingeniería debido a su excelente resistencia mecánica y resistencia a la radiación. Se utilizaron tubos de PEEK similares a los que componen los aislantes de cables de instrumentación y control en una Central Nuclear. Para evaluar su comportamiento al envejecimiento en este contexto se establecieron temperaturas de envejecimiento de 135 grados C correspondientes a un LOCA y de referencia a 25 grado C, en un período de 30 días. Se caracterizó al material por técnicas como DRx y DSC para establecer la evolución morfológica y su densidad con el envejecimiento. A los envejecidos a 135 grado C, además se los sometió a ensayos de tracción. Los resultados durante el envejecimiento demostraron aumento de la cristalinidad a 135 grado C comparado con 25 grados C.Durante el envejecimiento a 135 grados C se encontró una doble transición vítrea, que se relacionó con efectos a nivel intra e interesferulíticos, particularmente su influencia sobre los mecanismos de deformación plástica por deslizamiento y en bloque. En todos los tubos sometidos a tracción se obtuvo 'cold drawing'. Finalmente, se propuso un modelo que permitió explicarlos cambios físicos producidos en el PEEK envejecido a 25 grados C y 135 grados C y los efectos sobre las propiedades mecánicas.
Sumario, etc. PEEK is a linear thermoplastic developed for special engineering purposes due to its excellent mechanical strength and radiation resistance. For this work PEEK tubes similar to those used for the insulation of instrumentation and control cables in a Nuclear Power Plant were used. To evaluate their behavior aging over a period of 30 days at 135 grados C, corresponding to a LOCA, and 25 grados C as a reference of the on shelf storage were applied. Changes in the morphology and density along the aging process were followed by XRD and DSC. Samples aged at 135 grados C were also subjected to tensile tests. Experimental results demonstrated that crystalline degree of samples aged at 135 grados C was higher than for samples aged at 25 grados C. Double glass transitions, measured in PEEK samples aged at 135 grados C, was related to intra and inter spherulitic mechanisms. Tensile curves of all the aged samples showed "cold drawing". Finally, a model of the physical changes produced in PEEK aged at 25 grados C and 135 grados C and its effects on the mechanical properties has been presented.
590 ## - NOTA LOCAL (RLIN)
Nota local Observaciones: Solo formato electrónico
Nota local Lugar de trabajo: Centro Atomico Constituyentes
653 ## - TÉRMINO DE INDIZACIÓN--NO CONTROLADO
Término no controlado envejecimiento térmico
Término no controlado cold drawing
Término no controlado polímero semicristalino
Término no controlado PEEK
Término no controlado thermal aging
Término no controlado cold drawing
Término no controlado semicrystalline polymers
Término no controlado PEEK
710 1# - ENTRADA AGREGADA--NOMBRE DE ENTIDAD CORPORATIVA
Nombre de entidad corporativa o nombre de jurisdicción como elemento de entrada Comisión Nacional de Energía Atómica.
Unidad subordinada Instituto de Tecnología Sabato.
Nombre de entidad corporativa o nombre de jurisdicción como elemento de entrada Universidad Nacional de San Martín.
Holdings
Estatus retirado Estado de pérdida Fuente de la clasificación o esquema de estantería Estado de daño No para préstamo Biblioteca de origen Biblioteca actual Fecha de adquisición Número de inventario Signatura topográfica completa Código de barras Visto por última vez Precio de reemplazo Tipo de ítem Koha
    Dewey Decimal Classification     Centro de Información Eduardo Savino Centro de Información Eduardo Savino 02/10/2018 IS/T--161/15 IS/T--161/15 IS/T--161/15 02/10/2018 02/10/2018 Thesis