Interacción entre precipitados y la transformación martensítica en monocristales de CuAlNi con memoria de forma. (Record no. 27003)

MARC details
000 -LEADER
campo de control de longitud fija 04380mm aa2200337a 44500
003 - IDENTIFICADOR DE NÚMERO DE CONTROL
campo de control AR-SmCIES
005 - FECHA Y HORA DE LA ÚLTIMA TRANSACCIÓN
campo de control 20181026094009.0
008 - DATOS DE LONGITUD FIJA--INFORMACIÓN GENERAL
campo de control de longitud fija 160322s2015 ag fq d # spa#d
040 ## - FUENTE DE CATALOGACIÓN
Centro catalogador/agencia de origen AR-SmCIES
Centro/agencia transcriptor AR-SmCIES
100 1# - ENTRADA PRINCIPAL--NOMBRE DE PERSONA
Nombre de persona Herschberg, Rafael
9 (RLIN) 1351
245 10 - MENCIÓN DEL TÍTULO
Título Interacción entre precipitados y la transformación martensítica en monocristales de CuAlNi con memoria de forma.
246 11 - FORMA VARIANTE DEL TITULO
Título propio/Titulo breve Interaction between precipitates and martensitic transformation in shape memory CuAlNi single crystals.
260 ## - PUBLICACIÓN, DISTRIBUCIÓN, ETC.
Fecha de publicación, distribución, etc. 2015.
300 ## - DESCRIPCIÓN FÍSICA
Dimensiones 86 p.
500 ## - NOTA GENERAL
Nota general Cantidad de ejemplares: 1
502 ## - NOTA DE TESIS
Nota de tesis Tesis para optar al título de Magister en Ciencia y Tecnología de Materiales. Director/es: Gastian, Rosana; Zelaya, Eugenia
520 ## - RESUMEN, ETC.
Sumario, etc. Para cierto rango de composiciones químicas de CuAlNi, esta aleación exhibe los efectos memoria de forma y pseudoelástico. Estos son producto de una transformación martensítica [TM] termoelástica inducida desde una fase Beta de alta temperatura obtenida a temperatura ambiente en forma metaestable. Esta transformación martensítica puede ser inducida por enfriamiento o por aplicación de carga mecánica. Las aleaciones de CuAlNi son promisorias para su uso como núcleo actuador en dispositivos que tengan que funcionar a altas temperaturas. Por lo tanto, resulta interesante investigar la respuesta termo-mecánica de estas aleaciones para su uso específico a determinados rangos de temperaturas. Para esto, se estudian las aleaciones luego de ser sometidas a diversos tratamientos térmicos de envejecimiento. En este trabajo se abordó el estudio de la respuesta termo-mecánica de monocristales de Cu-14.3 por ciento Al-4.1 por ciento Ni [por ciento peso] junto con un análisis de la microestructura luego de someterlos a envejecimientos a 200 ºC y 250 ºC estando el material en fase ß. A raíz de estos tratamientos térmicos se produce la precipitación de fases estables, con lo cual es primordial estudiar la interacción entre estos precipitados y las transformaciones martensíticas inducidas para comprender el comportamiento del material. Para este análisis se utilizaron técnicas de difracción de rayos X, mediciones de resistencia eléctrica en función de la temperatura, ensayos mecánicos de tracción, microscopía óptica, microscopía electrónica de barrido [SEM] y microscopía electrónica de transmisión [TEM].
Sumario, etc. For a well-defined chemical composition range of CuAlNi, this alloy exhibits shape memory and pseudoelastic effects. Both effects are products of a thermoelastic martensitic transformation [MT] induced from a high temperature ß phase obtained at room temperature in a metastable state. The martensitic transformation can be induced by cooling or by means of an applied mechanical load. CuAlNi alloys are promising for their use in actuator devices that work at high temperatures. Therefore, it is interesting to study its thermomechanical response for its specific use at determined ranges of temperature. So, the alloys are studied after being subjected to different thermal aging treatments. In this work the thermomechanical response of Cu-14.3 per cent Al-4.1 per cent Ni [per cent wt.] single crystals was studied with a microstructural analysis after thermal treatments at 200 ºC and 250 ºC applied to the Betha phase. Due to the thermal treatments, the precipitation of stable phases occurs. For this reason, it is imperative to study the interaction between the precipitates and the martensitic transformation induced in the alloy in order to understand the material behavior. For the analysis, the following techniques were used: X-ray diffraction, electrical resistance vs. temperature measurements, tensile tests, optical microscopy, scanning electron microscopy [SEM] and transmission electron microscopy [TEM].
590 ## - NOTA LOCAL (RLIN)
Nota local Lugar de trabajo: Centro Atomico Constituyentes
653 ## - TÉRMINO DE INDIZACIÓN--NO CONTROLADO
Término no controlado Materiales con memoria de forma
Término no controlado Aleaciones base cobre
Término no controlado Transformaciones martensíticas
Término no controlado Tratamientos térmicos
Término no controlado Precipitación
Término no controlado Shape memory materials
Término no controlado Copper base alloys
Término no controlado Martensitic transformations
Término no controlado Thermal treatments
Término no controlado Precipitation
710 1# - ENTRADA AGREGADA--NOMBRE DE ENTIDAD CORPORATIVA
Nombre de entidad corporativa o nombre de jurisdicción como elemento de entrada Comisión Nacional de Energía Atómica.
Unidad subordinada Instituto de Tecnología Sabato.
9 (RLIN) 1034
Nombre de entidad corporativa o nombre de jurisdicción como elemento de entrada Universidad Nacional de San Martín.
9 (RLIN) 1033
942 ## - ELEMENTOS DE ENTRADA SECUNDARIOS (KOHA)
Fuente de la clasificación o esquema de estantería Universal Decimal Classification
Tipo de ítem Koha Thesis
Holdings
Estatus retirado Estado de pérdida Fuente de la clasificación o esquema de estantería Estado de daño No para préstamo Biblioteca de origen Biblioteca actual Fecha de adquisición Número de inventario Signatura topográfica completa Código de barras Visto por última vez Precio de reemplazo Tipo de ítem Koha
    Dewey Decimal Classification     Centro de Información Eduardo Savino Centro de Información Eduardo Savino 02/10/2018 IS/T--157/15 IS/T--157/15 IS/T--157/15 02/10/2018 02/10/2018 Thesis