Materiales compuestos auto-reforzados basados en telas comerciales de polipropileno. (Record no. 26946)

MARC details
000 -LEADER
campo de control de longitud fija 06117mm aa2200253a 44500
000 - LEADER
campo de control de longitud fija aIS/T--148/14
003 - IDENTIFICADOR DE NÚMERO DE CONTROL
campo de control AR-SmCIES
008 - DATOS DE LONGITUD FIJA--INFORMACIÓN GENERAL
campo de control de longitud fija 150630s2014 ag fq d # spa#d
040 ## - FUENTE DE CATALOGACIÓN
Centro catalogador/agencia de origen AR-SmCIES
100 1# - ENTRADA PRINCIPAL--NOMBRE DE PERSONA
Nombre de persona Mijares, José Luis
245 10 - MENCIÓN DEL TÍTULO
Título Materiales compuestos auto-reforzados basados en telas comerciales de polipropileno.
246 11 - FORMA VARIANTE DEL TITULO
Título propio/Titulo breve Self-reinforced polymer composites based on polypropylene commercial fabrics.
260 ## - PUBLICACIÓN, DISTRIBUCIÓN, ETC.
Fecha de publicación, distribución, etc. 2014.
300 ## - DESCRIPCIÓN FÍSICA
Dimensiones 110 p.
500 ## - NOTA GENERAL
Nota general Cantidad de ejemplares: 1
502 ## - NOTA DE TESIS
Nota de tesis Tesis para optar al título de Magister en Ciencia y Tecnología de Materiales. Director/es: Mollo, Mariana; Bernal, Celina Raquel
520 ## - RESUMEN, ETC.
Sumario, etc. Los polímeros auto-reforzados compiten con los compuestos tradicionales en función de su relación performance/costo. La facilidad de reciclado y la posibilidad de obtener estructuras livianas son sus principales ventajas, por lo que pueden considerarse materiales amigables con el medio ambiente. Se plantea como objetivo principal del presente trabajo de tesis desarrollar compuestos auto-reforzados trabajando con un sistema polimérico basado en polipropileno [PP], utilizando como refuerzos telas comerciales tejidas y no tejidas. Se obtuvieron y estudiaron compuestos auto-reforzados con las siguientes composiciones y procesamientos: [i] matriz de PP copolímero al azar y refuerzo de PP no tejido por la técnica de apilamiento de láminas; [ii] matriz de PP copolímero al azar y refuerzo combinado de PP no tejido y rafia de PP por la técnica de apilamiento de láminas; [iii] combinación de PP no tejido y rafia de PP por la técnica de compactación en caliente. La utilización de PP no tejido como refuerzo aumenta la rigidez del material. Sin embargo, no se observó una mejora apreciable en otros parámetros de tracción e impacto. En los materiales compuestos obtenidos por apilamiento de láminas con refuerzo combinado de telas de PP tejidas y no tejidas, se observaron las mejores propiedades de tracción e impacto para el material procesado a 155 grado C. El agregado de la rafia mejora en forma apreciable la resistencia al impacto. El compuesto auto-reforzado obtenido por compactación en caliente de láminas de PP no tejido y rafia de PP, procesado a 165 grado C, es el que presentó mejores propiedades de tracción e impacto, siendo el más promisorio para aplicaciones estructurales. Se estudió el comportamiento a la fractura y la falla a los compuestos reforzados con PP no tejido y rafia de PP, adoptándose el parámetro J en la inestabilidad para caracterizar el comportamiento a fractura. El compuesto obtenido por compactación en caliente exhibió una resistencia mucho mayor que el compuesto obtenido por apilamiento de láminas. Ambos compuestos fallaron por delaminación y arranque de los refuerzos. Como conclusión general puede afirmarse que el PP no tejido por sí solo no es un refuerzo efectivo para la obtención de materiales compuestos auto-reforzados basados en PP. Sin embargo, su combinación con una tela tejida de PP, como la rafia, brinda resultados alentadores respecto a sus propiedades mecánicas, particularmente en lo que respecta a su resistencia a la tracción, tenacidad al impacto y comportamiento a la fractura.
Sumario, etc. Self-reinforced polymers compete with traditional composites in different applications depending on their performance/cost ratio. Among other advantages, they can be considered environmentally friendly materials, being easily recyclable, and their lower density, compared to other composites, can be exploited to obtain light parts and structures. The main objective of this thesis is to develop self-reinforced polymer composites based on polypropylene [PP] using woven and non-woven commercial fabrics as reinforcement. Different self-reinforced polymer composites were obtained by using several processing methods and subsequently characterized. [i] PP random copolymer matrix with PP non-woven as reinforcement was prepared by the film-stacking technique followed by compression molding; [ii] PP random copolymer matrix with combined PP woven and non-woven fabrics as reinforcement were obtained by the film stacking technique followed by compression molding; and [iii] PP woven and non-woven fabrics were consolidated by the hot compaction technique. When PP non-woven fabrics were only used as reinforcement, increased material stiffness was found. However, no significant enhancement in other tensile parameters and impact properties were observed. For self-reinforced composites obtained by film stacking using combined PP woven and non-woven fabrics as reinforcement, the best tensile and impact properties were observed for the material processed at 155 C degrees. Incorporation of PP woven fabrics significantly improved impact resistance. Self-reinforced composites obtained by hot compaction of PP woven and non-woven fabrics, consolidated at 165 C degrees, exhibited the best tensile and impact properties, being the most promising material for structural applications. The fracture and failure behavior of composites reinforced with PP woven and non-woven fabrics, was studied adopting the J parameter at instability for fracture characterization. The composite obtained by hot compaction showed much more resistance to unstable crack propagation than composite obtained by film stacking. Both composites failed by delamination and pull-out of reinforcement. As a general conclusion it can be said that PP non-woven fabric alone is not an effective reinforcement for self-reinforced PP-based polymer composites. However, when combining this reinforcement with a PP woven fabric, encouraging results were obtained regarding their mechanical properties, particularly their tensile strength, impact toughness and fracture resistance.
590 ## - NOTA LOCAL (RLIN)
Nota local Lugar de trabajo: Instituto Nacional de Tecnología Industrial
653 ## - TÉRMINO DE INDIZACIÓN--NO CONTROLADO
Término no controlado polímeros auto-reforzados
Término no controlado polipropileno
Término no controlado materiales compuestos
710 1# - ENTRADA AGREGADA--NOMBRE DE ENTIDAD CORPORATIVA
Nombre de entidad corporativa o nombre de jurisdicción como elemento de entrada Comisión Nacional de Energía Atómica.
Unidad subordinada Instituto de Tecnología Sabato.
Nombre de entidad corporativa o nombre de jurisdicción como elemento de entrada Universidad Nacional de San Martín.
Holdings
Estatus retirado Estado de pérdida Fuente de la clasificación o esquema de estantería Estado de daño No para préstamo Biblioteca de origen Biblioteca actual Fecha de adquisición Número de inventario Signatura topográfica completa Código de barras Visto por última vez Precio de reemplazo Tipo de ítem Koha
    Dewey Decimal Classification     Centro de Información Eduardo Savino Centro de Información Eduardo Savino 02/10/2018 IS/T--148/14 IS/T--148/14 IS/T--148/14 02/10/2018 02/10/2018 Thesis