Estudio de la oxidación de la fase de laves Zr(Cr,Fe)_2. (Record no. 26857)

MARC details
000 -LEADER
campo de control de longitud fija 02832mm aa2200205a 44500
000 - LEADER
campo de control de longitud fija aIT/T--60/01
003 - IDENTIFICADOR DE NÚMERO DE CONTROL
campo de control AR-SmCIES
008 - DATOS DE LONGITUD FIJA--INFORMACIÓN GENERAL
campo de control de longitud fija 020715s2001 ag fq d # spa#d
040 ## - FUENTE DE CATALOGACIÓN
Centro catalogador/agencia de origen AR-SmCIES
100 1# - ENTRADA PRINCIPAL--NOMBRE DE PERSONA
Nombre de persona Saporiti, M. Fabiana S.
245 10 - MENCIÓN DEL TÍTULO
Título Estudio de la oxidación de la fase de laves Zr(Cr,Fe)_2.
260 ## - PUBLICACIÓN, DISTRIBUCIÓN, ETC.
Fecha de publicación, distribución, etc. 2001.
300 ## - DESCRIPCIÓN FÍSICA
Dimensiones 75 p.
500 ## - NOTA GENERAL
Nota general Cantidad de ejemplares: 1
502 ## - NOTA DE TESIS
Nota de tesis Tesis para optar al título de Magister en Ciencia y Tecnología de Materiales. Director/es: Versaci, Raúl A.; Bozzano, Patricia B.
520 ## - RESUMEN, ETC.
Sumario, etc. Con la finalidad de estudiar la oxidación de la fase de Laves Zr(Cr_x,Fe_1-x)_2 con estructura C15 se fabricaron en un horno de arco bajo atmósfera de Argón dos aleaciones de composición Zr(Cr_0.95,Fe_0.05)_2 y Zr(Cr_0.15,Fe_0.85)_2. Los elementos utilizado para realizar las aleaciones son de pureza comercial. Las muestras fundidas fueron examinadas por microscopía óptica, microscopía electrónica de barrido (SEM), microscopía electrónica de transmisión (TEM). También fueron analizadas por difracción de Rayos X (RX), espectroscopía Mössbauer (MS) y las composiciones fueron medidas por microanálisis cuantitativo en microsonda eletrónica (EPMA) a temperatura ambiente. Se determinó en ambas muestras que en el proceso de oxidación, se produce una oxidación selectiva de los elementos que la constituyen. En ambas aleaciones se estableció que el óxido estaba formado por las siguientes fases: fase de Laves original, circonia monoclínica, circonia tetragonal, (Cr,Fe)_2O_3 y Cr en la muestra rica en Cr y la presencia de: fase de Laves original, circonia monoclínica, circonia tetragonal, alfa-Fe_2O_3, alfa-Fe en la muestra rica en Fe.
Sumario, etc. Two alloys with composition Zr(Cr_0.95,Fe_0.05)_2 Zr(Cr_0.15,Fe_0.85)_2 were arc furnaced under argon atmosphere in orther to study the C15 Laves phase Zr(Cr_x,Fe_1-x)_2 oxidation. Materials of commercial purity were used. The alloys were examined by optical microscopy, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). they were also analyzed at room temperature by electron-probe microanalysis (EPMA), Mössbauer spectroscopy (MS) and X-ray diffraction (XRD). In both samples it was determined that a selective oxidation of the constitutive elements occurs during the oxidation process. It was also established that the oxide in both alloys was composed of the following phases: original Laves phase, monoclinic zirconia, tetragonal zirconia, (Cr,Fe)_2O_3 and Cr, in the rich Cr alloy and the presence of original Laves phase, monoclinic zirconia, tetragonal zirconia, alpha-Fe_2O_3 and alpha-Fe in the rich Fe alloy.
590 ## - NOTA LOCAL (RLIN)
Nota local Lugar de trabajo: CAC
710 1# - ENTRADA AGREGADA--NOMBRE DE ENTIDAD CORPORATIVA
Nombre de entidad corporativa o nombre de jurisdicción como elemento de entrada Comisión Nacional de Energía Atómica.
Unidad subordinada Instituto de Tecnología Sabato.
Nombre de entidad corporativa o nombre de jurisdicción como elemento de entrada Universidad Nacional de San Martín.
Holdings
Estatus retirado Estado de pérdida Fuente de la clasificación o esquema de estantería Estado de daño No para préstamo Biblioteca de origen Biblioteca actual Fecha de adquisición Número de inventario Signatura topográfica completa Código de barras Visto por última vez Precio de reemplazo Tipo de ítem Koha
    Dewey Decimal Classification     Centro de Información Eduardo Savino Centro de Información Eduardo Savino 02/10/2018 IT/T--60/01 IT/T--60/01 IT/T--60/01 02/10/2018 02/10/2018 Thesis